Polymer Property : Thermal Conductivity = 14.7 W/m-K Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Thermal Conductivity	14.7 W/m-K @Temperature 316 Â°C	102 BTU-in/hr-ftÂ²-Â°F @Temperature 601 Â°F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	14.7 W/m-K @Temperature 316 Â°C	102 BTU-in/hr-ftÂ²-Â°F @Temperature 601 Â°F
Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	14.7 W/m-K @Temperature 316 Â°C	102 BTU-in/hr-ftÂ²-Â°F @Temperature 601 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	14.7 W/m-K @Temperature 316 Â°C	102 BTU-in/hr-ftÂ²-Â°F @Temperature 601 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	14.7 W/m-K @Temperature 316 Â°C	102 BTU-in/hr-ftÂ²-Â°F @Temperature 601 Â°F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	14.7 W/m-K @Temperature 316 Â°C	102 BTU-in/hr-ftÂ²-Â°F @Temperature 601 Â°F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121Â°C, air cooled, aged 16 hours at 899Â°C Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	14.7 W/m-K @Temperature 100 °C	102 BTU-in/hr-ft²-°F @Temperature 212 °F	Hardened Condition
Bohler-Uddeholm BÖHLER W302 SUPERIOR® Premium H13 Tool Steel A premium grade H13 hot work tool steel featuring:Very good toughness properties meeting the requirements of NADCA 207-97, and the superior quality levels of NADCA 207-2003Very good heat checking re..
Thermal Conductivity	14.7 W/m-K @Temperature 316 °C	102 BTU-in/hr-ft²-°F @Temperature 601 °F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include ..