Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, all-weld metal, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, mill annealed HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 25.4 mm thick bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet, GTAW weld HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 30% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 50% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 50% cold rolled and 1 hour at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 50% cold rolled and 5000 hours at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 6.4 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 9.5 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, all-weld metal, GMAW weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, plate and bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 23.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
|
Special Metals INCONEL® alloy 740 Precipitation-Hardenable Ni-Cr-Co Superalloy INCONEL® alloy 740 is a nickel-chromium-cobalt alloy developed by Special Metals Corporation. The alloy is age hardenable by the precipitation of a gamma prime second phase. Potential applicati.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 0.71 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 10% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 19.1 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 31.8 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
Thermal Conductivity | 10.2 W/m-K @Temperature 24.0 °C |
70.8 BTU-in/hr-ft²-°F @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |