Polymer Property : Thermal Conductivity = 96.5 BTU-in/hr-ft²-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Thermal Conductivity	13.9 W/m-K	96.5 BTU-in/hr-ft²-°F	RT
Outokumpu 4878 High Temperature Austenitic Stainless Steel Heat-resistant variant of 1.4541, with a slightly higher max carbon content. Recommended max service temperature for this steel in dry air is 800°C. Applications: Heat and creep resistance. For ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, 10% cold reduction, 1010Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, 20% cold reduction, 1120Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, 30% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, 30% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, 40% cold reduction, 1120Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, 50% cold reduction, 1010Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, 50% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, hot rolled and 1050Â°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, plate after 1000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, plate after 1000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, plate after 16000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, plate after 16000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, plate after 16000 hours at 870Â°C (1600Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, plate after 4000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, plate after 4000 hours at 870Â°C (1600Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, plate after 8000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, plate after 8000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, plate after 8000 hours at 870Â°C (1600Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 Â°C	96.5 BTU-in/hr-ftÂ²-Â°F @Temperature 572 Â°F
Haynes 625 alloy, plate, as annealed at 1025Â°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	13.9 W/m-K @Temperature 300 °C	96.5 BTU-in/hr-ft²-°F @Temperature 572 °F
Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	13.9 W/m-K @Temperature 300 °C	96.5 BTU-in/hr-ft²-°F @Temperature 572 °F
Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	13.9 W/m-K @Temperature 300 °C	96.5 BTU-in/hr-ft²-°F @Temperature 572 °F
Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	13.9 W/m-K @Temperature 300 °C	96.5 BTU-in/hr-ft²-°F @Temperature 572 °F
Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	13.9 W/m-K @Temperature 300 °C	96.5 BTU-in/hr-ft²-°F @Temperature 572 °F
Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var..
Thermal Conductivity	13.9 W/m-K @Temperature 300 °C	96.5 BTU-in/hr-ft²-°F @Temperature 572 °F
Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	13.9 W/m-K @Temperature 300 °C	96.5 BTU-in/hr-ft²-°F @Temperature 572 °F
Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	13.9 W/m-K @Temperature 300 °C	96.5 BTU-in/hr-ft²-°F @Temperature 572 °F
Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..