Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 0% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 30% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, plate, 1000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, plate, 4000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, plate, 8000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 12.4 W/m-K | 86.1 BTU-in/hr-ft²-°F | |
Special Metals INCOLOY® Alloy 330 A nickel-iron-chromium alloy with an addition of silicon for enhanced oxidation resistance. It has good strength at high temperatures and excellent resistance to carburizing and oxidizing atmospher.. |
|||
Thermal Conductivity | 12.4 W/m-K | 86.1 BTU-in/hr-ft²-°F | |
Special Metals NILO® 365 Controlled-Expansion Alloy For the manufacture of tooling for composites, the NILO® nickel-iron alloys offer a unique combination of matched thermal expansion to avoid warping during the curing cycle, along with strength, .. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 12.4 W/m-K @Temperature 200 °C |
86.1 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |