- Polymer Property : Thermal Conductivity = 183 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 183 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 0% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 30% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 26.3 W/m-K @Temperature 500 °C |
183 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Crucible Steel CPM® 10V® (AISI A11) Tool Steel CPM 10V was the first in the family of high vanadium tool steels made by the Crucible Particle Metallurgy process. Crucible engineers optimized the vanadium content to provide superior wear resistan.. |
|||
| Thermal Conductivity | 26.4 W/m-K | 183 BTU-in/hr-ft²-°F | |
| California Fine Wire Manganin 290 Copper, Manganese, and Nickel Resistance Wire All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 26.4 W/m-K @Temperature 900 °C |
183 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||