- Polymer Property : Thermal Conductivity = 16.9 W/m-K
Polymer Property : Thermal Conductivity = 16.9 W/m-K Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| HP Alloys Alloy X, 30% Cold Worked 30% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, and Haynes International. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| HP Alloys Alloy X, 15% Cold Worked 15% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, and Haynes International. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| HP Alloys Alloy X, 5% Cold Worked 5% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, and Haynes International. |
|||
| Thermal Conductivity | 16.9 W/m-K @Temperature 50.0 °C |
117 BTU-in/hr-ft²-°F @Temperature 122 °F |
|
| Special Metals INCOLOY® Alloy 903 A nickel-iron-cobalt alloy with additions of niobium, titanium, and aluminum for precipitation hardening. The alloy combines high strength with a low and constant coefficient of thermal expansion a.. |
|||