Polymer Property : Thermal Conductivity = 15.3 W/m-K Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, 20% cold reduction, 1010Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, 20% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, 20% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, 30% cold reduction, 1120Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, 30% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, 40% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, 40% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, 50% cold reduction, 1010Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, 50% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, 50% cold reduction, 1175Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, hot rolled and 1050Â°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, plate after 1000 hours at 650Â°C (1200Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, plate after 1000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, plate after 1000 hours at 870Â°C (1600Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, plate after 16000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, plate after 4000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, plate after 4000 hours at 870Â°C (1600Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, plate after 8000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 400 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes 625 alloy, plate after 8000 hours at 870Â°C (1600Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Thermal Conductivity	15.3 W/m-K @Temperature 20.0 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 68.0 Â°F
Schmolz + Bickenbach UGIMA 303 UXÂ® Stainless Steel Bar Description: 303 UGIMA UXÂ® is an improved machining grade produced only by Ugitech, providing the ultimate level of machinability available in an austenitic stainless steel. 303 UGIMA UXÂ® feat..
Thermal Conductivity	15.3 W/m-K @Temperature 20.0 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 68.0 Â°F
Schmolz + Bickenbach UGIMAÂ® 303 HD Stainless Steel Bar Description: 303 UGIMA HDâ„¢ is a low sulfur version of Ugitechâ€™s improved machining 303 grade. It is designed to provide better metallurgical performance with respect to weldability, corros..
Thermal Conductivity	15.3 W/m-K @Temperature 20.0 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 68.0 Â°F
Schmolz + Bickenbach UGIMAÂ® 303 Stainless Steel Bar Description: 303 UGIMAÂ® is Ugitechâ€™s improved machining grade produced only by Ugitech. It is identical in every way to regular 303, except with respect to machinability. 303 UGIMAÂ® repre..
Thermal Conductivity	15.3 W/m-K @Temperature 20.0 Â°C	106 BTU-in/hr-ftÂ²-Â°F @Temperature 68.0 Â°F
Schmolz + Bickenbach UGIMAÂ® 316/316L Stainless Steel Bar Description: 316/316L UGIMAÂ® is Ugitechâ€™s improved machining grade produced only by Ugitech. It is identical in every way to regular 316L, except with respect to machinability. 316/316L UGIM..
Thermal Conductivity	15.3 W/m-K @Temperature 400 °C	106 BTU-in/hr-ft²-°F @Temperature 752 °F
Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	15.3 W/m-K @Temperature 400 °C	106 BTU-in/hr-ft²-°F @Temperature 752 °F
Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	15.3 W/m-K @Temperature 400 °C	106 BTU-in/hr-ft²-°F @Temperature 752 °F
Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	15.3 W/m-K @Temperature 400 °C	106 BTU-in/hr-ft²-°F @Temperature 752 °F
Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Thermal Conductivity	15.3 W/m-K @Temperature 400 °C	106 BTU-in/hr-ft²-°F @Temperature 752 °F
Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..