Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 20.9 W/m-K @Temperature 500 °C |
145 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Outokumpu 4762 High Temperature Ferritic Stainless Steel Highest chromium content-most resistant to reducing sulphurous gases. Susceptible to 475°C embrittlement and s-phase forms during long exposures in the range 600-800°C.Applications: Mostly used i.. |
|||
Thermal Conductivity | 20.9 W/m-K @Temperature 600 °C |
145 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 20.9 W/m-K @Temperature 600 °C |
145 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 20.9 W/m-K @Temperature 600 °C |
145 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 20.9 W/m-K @Temperature 600 °C |
145 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 20.9 W/m-K @Temperature 600 °C |
145 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 20.9 W/m-K @Temperature 600 °C |
145 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 20.9 W/m-K @Temperature 600 °C |
145 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 20.9 W/m-K @Temperature 600 °C |
145 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 20.9 W/m-K @Temperature 600 °C |
145 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 20.9 W/m-K @Temperature 100 °C |
145 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Schmolz + Bickenbach MoldMAX® SC Copper Alloy Description: Brush Wellman’s MoldMAX® SC is a high conductivity copper mold alloy with good strength. MoldMAX® SC is used as blow mold cavities, injection mold cores and cavities and hot .. |