Thermal Properties | Metric | English | Comments |
---|---|---|---|
Decomposition Temperature | 616 °C | 1140 °F | |
Daelim H&L Plavis N Aromatic Polyimide, Non-Filled, Direct Formed
(Unverified Data**) Information provided by Daelim H&L |
|||
Decomposition Temperature | 616 °C | 1140 °F | |
Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Direct Formed
(Unverified Data**) Information provided by Daelim H&L |
|||
Decomposition Temperature | 616 °C | 1140 °F | |
Daelim H&L Plavis G40 Aromatic Polyimide, 40% Graphite Filled, Direct Formed
(Unverified Data**) Information provided by Daelim H&L |
|||
Decomposition Temperature | 616 °C | 1140 °F | |
Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Machined Parts High abrasion resistance, very low friction coefficient property, suitable for being applied to spin component of spin apparatusInformation provided by Daelim H&L |
|||
Decomposition Temperature | 616 °C | 1140 °F | |
Daelim H&L Plavis G40 Aromatic Polyimide, 40% Graphite Filled, Machined Parts Higher abrasion resistance than G15, high value stability and very low friction coefficient propertyInformation provided by Daelim H&L |
|||
Decomposition Temperature | 616 °C | 1140 °F | |
Daelim H&L Plavis N Aromatic Polyimide, Non-Filled, Machined Parts Superior chemical property, very high radiation resistance, electrical and thermal property, low outgassing and superior physical propertyInformation provided by Daelim H&L |