Polymer Property : Deflection Temperature at 8.0 MPa = 110 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 8.0 MPa	80.0 - 110 °C	176 - 230 °F	ISO 75-C
Raschig Group AMPLA® 2000 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve..
Deflection Temperature at 8.0 MPa	80.0 - 110 °C	176 - 230 °F	Injection; ISO 75-C
Raschig Group AMPLA® 2500 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat..
Deflection Temperature at 8.0 MPa	80.0 - 110 °C	176 - 230 °F	Injection; ISO 75-C
Raschig Group AMPLA® 7250 melamine-modified polyester Cellulose reinforced melamine-modified Polyester molding compound. Very good electrical values, excellent heat resistance, excellent surface quality, low post shrinkage. This product meets the allow..
Deflection Temperature at 8.0 MPa	80.0 - 110 °C	176 - 230 °F	Average value: 86.0 °C Grade Count:5
Overview of materials for Nylon 12, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. ..