Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 448 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	231 °C	448 °F	ASTM D648
Nilit Polynil® N66-P50N Lubed Nylon 6/6 Information provided by US distributor Polymer Technology and Services, LLC (PTS).
Deflection Temperature at 0.46 MPa (66 psi)	231 Â°C @Thickness 3.20 mm	448 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP RBL36L PA 66 LNP* LUBRICOMP* RBL36L is a compound based on Nylon 66 containing 30% Glass Bead, 15% PTFE. Added features s of this grade are: Low Extractable, Wear Resistant.
Deflection Temperature at 0.46 MPa (66 psi)	231 Â°C @Thickness 3.20 mm	448 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 LNP* LUBRICOMP* RN001S is a compound based on Nylon 66 resin containing 2% MOS2. Added features of this material include: Wear Resistant, Heat Stabilized.
Deflection Temperature at 0.46 MPa (66 psi)	231 Â°C @Thickness 3.20 mm	448 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 (Asia Pacific) LNP* Lubricomp* RN001S is a compound based on Nylon 66 resin containing MOS2. Added features of this material include: Internally Lubricated, Heat Stabilized.
Deflection Temperature at 0.46 MPa (66 psi)	231 Â°C	448 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP JF008E PES LNP* THERMOCOMP* JF008E is a compound based on Polyethersulfone containing 40% Glass Fiber. Characteristics of this grade are: Easy Molding.
Deflection Temperature at 0.46 MPa (66 psi)	231 °C	448 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Be
Eurostar Staramide AK8 PA66, 40% Mineral Reinforced, Injection Molding Staramide AK8 is a 40% Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Deflection Temperature at 0.46 MPa (66 psi)	231 °C	448 °F	ISO 75
BASF Petra® 110 BK-112 15% Glass Filled PET Petra 110 is a 15% glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a good combination of performance properties including good strength a..
Deflection Temperature at 0.46 MPa (66 psi)	231 °C	448 °F	ASTM D648
Aaron Industries AAROPRENE® G/MFN 6602 Glass and Mineral Filled Nylon 6/6 AAROPRENE® GFN & MFN 6600 Series Reinforced CompoundsColor may be specified.