Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 164 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	73.3 °C	164 °F	ASTM D648
Plaskolite Vivak PETG Sheet VIVAK offers a balance of physical properties and ease of fabrication. It is ideally suited for complex parts requiring fabrication, including deep thermoforming draws and precise molded-in details...
Deflection Temperature at 0.46 MPa (66 psi)	73.1 Â°C	164 Â°F	ASTM D648
LyondellBasell AlathonÂ® M5352 High Density Polyethylene, Injection Molding Grade ALATHON M5352 is a high density copolymer with a narrow molecular weight distribution. This resin provides high impact strength and stress crack resistance, excellent color, low odor and good proces..
Deflection Temperature at 0.46 MPa (66 psi)	73.3 °C	164 °F	ASTM D648
ExxonMobil HDPE HD 6719.17 High Density Polyethylene Copolymer Resin Product Description: HD 6719 is a narrow molecular weight hexane copolymer designed for a wide rage of injection molding applications, combining easy processability with good toughness properties. I..
Deflection Temperature at 0.46 MPa (66 psi)	73.3 °C	164 °F	ASTM D648
ExxonMobil HDPE HD 6719.62 High Density Polyethylene Copolymer Resin Product Description: HD 6719 is a narrow molecular weight hexane copolymer designed for a wide rage of injection molding applications, combining easy processability with good toughness properties. I..
Deflection Temperature at 0.46 MPa (66 psi)	73.3 °C	164 °F	0.125";; ASTM D648
Diamond Polymers SBS 2160 Clear Styrene Butadiene Copolymer Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Deflection Temperature at 0.46 MPa (66 psi)	73.5 °C	164 °F	CP-TM-12
PolyOne Elastamax HTE 2101-1000 Polyurethane Alloy (discontinued **) This is an extrusion grade polyurethane alloy. Physical Form: Pellet. Standard Color: Off white, opaque.Information provided by M. A. Hanna. M. A. Hanna and Geon merged to form PolyOne in 2000. ..