- Polymer Property : CTE, linear = 9.67 µin/in-°F
Polymer Property : CTE, linear = 9.67 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.4 µm/m-°C @Temperature 0.000 - 1000 °C |
9.67 µin/in-°F @Temperature 32.0 - 1830 °F |
|
| Kennametal Stellite Stellite® 6 PM cast Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 0.000 - 1000 °C |
9.67 µin/in-°F @Temperature 32.0 - 1830 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 0.000 - 1000 °C |
9.67 µin/in-°F @Temperature 32.0 - 1830 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 15.9 mm thick bar Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 0.000 - 1000 °C |
9.67 µin/in-°F @Temperature 32.0 - 1830 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 0.000 - 1000 °C |
9.67 µin/in-°F @Temperature 32.0 - 1830 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 0.000 - 1000 °C |
9.67 µin/in-°F @Temperature 32.0 - 1830 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 0.000 - 1000 °C |
9.67 µin/in-°F @Temperature 32.0 - 1830 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 20.0 - 1000 °C |
9.67 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Haynes 625SQ® Nickel Alloy Sheet Haynes 625SQ alloy is a solid-solution strengthened superalloy. It is a modification of Haynes 625 alloy designed to enhance resistance to fatigue at temperatures up to approximately 1200°F (649Â.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 25.0 - 1000 °C |
9.67 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 17.4 µm/m-°C @Temperature 0.000 - 1000 °C |
9.67 µin/in-°F @Temperature 32.0 - 1830 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||