| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.9 µm/m-°C @Temperature 20.0 - 1000 °C |
9.39 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Kennametal Stellite Stellite® 19 Can be machined with carbide tipped tools, but when hardness exceeds Rc55 it is best to grind. Applications include cutting tools, bearing races, guide rolls, and nozzle discs. Excellent resistance .. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6 PM cast Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6 PM with P/M Processing Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 15.9 mm thick bar Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.7 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 25.0 - 700 °C |
9.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 25.0 - 700 °C |
9.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 25.0 - 700 °C |
9.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-120® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 27.0 - 300 °C |
9.39 µin/in-°F @Temperature 80.6 - 572 °F |
Mean |
| Special Metals INCOLOY® A-286 Iron-Nickel-Chromium Alloy Data provided by the manufacturer, Special Metals. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 100 °C |
9.39 µin/in-°F @Temperature 32.0 - 212 °F |
|
| AK Steel 304 Austenitic Stainless steel AK Steel 304 is a variation of the basic 18-8 grade, Type 302. Lower carbon, in Type 304, minimizes chromium carbide precipitation due to welding and its susceptibility to intergranular corrosion. .. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature <=538 °C |
9.39 µin/in-°F @Temperature <=1000 °F |
|
| AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition A AK Steel 15-7 Mo® provides high strength and hardness, good corrosion resistance and minimum distortion on heat treatment. It is easily formed in the annealed condition and develops effective bala.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 20.0 - 982 °C |
9.39 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Kennametal Stellite Stellite® 25 Cobalt Chromium Cast Alloy Stellite alloy 25 forms a protective oxide film during hot metal-on metal wear which prevents metal transfer and damage due to adhesion. The alloy is resistant to thermal cracking and surface fatig.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||