- Polymer Property : CTE, linear = 8.72 µin/in-°F
Polymer Property : CTE, linear = 8.72 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.7 - 16.7 µm/m-°C @Temperature 20.0 - 200 °C |
8.72 - 9.28 µin/in-°F @Temperature 68.0 - 392 °F |
|
| PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
| CTE, linear | 15.7 - 16.7 µm/m-°C @Temperature 20.0 - 200 °C |
8.72 - 9.28 µin/in-°F @Temperature 68.0 - 392 °F |
|
| PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition T4 Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 21.1 - 649 °C |
8.72 µin/in-°F @Temperature 70.0 - 1200 °F |
|
| Kennametal Stellite Stellite® 31 PM cast Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy, 0% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 700 °C |
8.72 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 21.0 - 538 °C |
8.72 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Latrobe MP35N® Alloy MP35N is a nickel-cobalt base alloy of the Multiphase alloy system that has a unique combination of properties - ultra high strength, toughness, ductility, and outstanding corrosion resistance. The .. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 700 °C |
8.72 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 21.0 - 538 °C |
8.72 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 55% Cold Reduction Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 21.0 - 538 °C |
8.72 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, Cold Drawn 53%, Aged 565°C/4hr/AC Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 21.1 - 649 °C |
8.72 µin/in-°F @Temperature 70.0 - 1200 °F |
|
| Kennametal Stellite Stellite® 31 PM cast aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||