Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 14.7 µm/m-°C @Temperature 0.000 - 400 °C |
8.17 µin/in-°F @Temperature 32.0 - 752 °F |
|
Kennametal Stellite Stellite® 6 PM with P/M Processing Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 0.000 - 400 °C |
8.17 µin/in-°F @Temperature 32.0 - 752 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 15.9 mm thick bar Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 0.000 - 400 °C |
8.17 µin/in-°F @Temperature 32.0 - 752 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 0.000 - 400 °C |
8.17 µin/in-°F @Temperature 32.0 - 752 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 20.0 - 500 °C |
8.17 µin/in-°F @Temperature 68.0 - 932 °F |
|
Industeel CREUSABRO® 4800 Advanced Technology in Wear Steel Description: CREUSABRO® 4800(P) is a wear resistant steel offering up to 50% extra in service life compared with a 400 HB water quenched steel. CREUSABRO® 4800(P) combines several modern metal.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 760 °C |
8.17 µin/in-°F @Temperature 69.8 - 1400 °F |
|
Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 500 °C |
8.17 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
Special Metals DURANICKEL® 301 (UNS N03301) Annealed and Aged Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Annealed and Aged Strip specifically. Other property values are typical of aged DURANICKEL® alloy 301 or.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 500 °C |
8.17 µin/in-°F @Temperature 69.8 - 932 °F |
Mean; aged |
Special Metals DURANICKEL® 301 (UNS N03301) Annealed Rod and Bar Tensile strength (ultimate and yield), compressive strength, hardness, and elongation values reported here are typical for Annealed Rod and Bar specifically. Other property values are typical of ann.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 500 °C |
8.17 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
Special Metals DURANICKEL® 301 (UNS N03301) Half-Hard and Aged Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Half-Hard and Aged Strip specifically. Other property values are typical of aged DURANICKEL® alloy 301 o.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 500 °C |
8.17 µin/in-°F @Temperature 69.8 - 932 °F |
Mean; aged |
Special Metals DURANICKEL® 301 (UNS N03301) Half-Hard Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Half-Hard Strip specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 500 °C |
8.17 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
Special Metals DURANICKEL® 301 (UNS N03301) Spring Strip, Aged Tensile strength (ultimate), hardness, and elongation values reported here are typical for Spring Strip, Aged specifically. Other property values are typical of aged DURANICKEL® alloy 301 or the .. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 20.0 - 500 °C |
8.17 µin/in-°F @Temperature 68.0 - 932 °F |
Mean |
Special Metals INCONEL® HX Nickel Superalloy Data provided by the manufacturer, Special Metals. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 20.0 - 100 °C |
8.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum AL 20™ Sheet and Strip Specialty Steel The N08020 alloy has been available for many years and has found applications in many environments, such as in chlorides and in sulfuric and sulfurous acids.Although AL 20 alloy was developed for im.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 760 °C |
8.17 µin/in-°F @Temperature 69.8 - 1400 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 760 °C |
8.17 µin/in-°F @Temperature 69.8 - 1400 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 760 °C |
8.17 µin/in-°F @Temperature 69.8 - 1400 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |