Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 200 °C |
7.39 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 200 °C |
7.39 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 214® alloy, 20% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 200 °C |
7.39 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 214® alloy, 20% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 200 °C |
7.39 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 200 °C |
7.39 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 200 °C |
7.39 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 214® alloy, sheet, 32 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 300 °C |
7.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 300 °C |
7.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 230® alloy, 30% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 300 °C |
7.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 200 °C |
7.39 µin/in-°F @Temperature 77.0 - 392 °F |
|
Haynes 214® alloy, 10% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 600 °C |
7.39 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 24.0 - 427 °C |
7.39 µin/in-°F @Temperature 75.2 - 801 °F |
|
Haynes Hastelloy® C-22® alloy, 20% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 24.0 - 427 °C |
7.39 µin/in-°F @Temperature 75.2 - 801 °F |
|
Haynes Hastelloy® C-22® alloy, GTAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 24.0 - 427 °C |
7.39 µin/in-°F @Temperature 75.2 - 801 °F |
|
Haynes Hastelloy® C-22® alloy, SMAW weld, C-22 base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 600 °C |
7.39 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 21.0 - 300 °C |
7.39 µin/in-°F @Temperature 69.8 - 572 °F |
Mean |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 20% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 21.0 - 300 °C |
7.39 µin/in-°F @Temperature 69.8 - 572 °F |
Mean |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC. This produces ASTM grain size 9.5. Other property values are ty.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 100 °C |
7.39 µin/in-°F @Temperature 68.0 - 212 °F |
Mean |
Special Metals INCONEL® HX Nickel Superalloy Data provided by the manufacturer, Special Metals. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 21.1 - 93.3 °C |
7.40 µin/in-°F @Temperature 70.0 - 200 °F |
|
Carlson C 600 Nickel-Chromium-Iron Alloy Carlson Alloy C 600 is nickel-chromium alloy, developed for use in severely corrosive environments at elevated temperatures. The high nickel content of this alloy provides excellent resistance to c.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 300 °C |
7.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 24.0 - 427 °C |
7.39 µin/in-°F @Temperature 75.2 - 801 °F |
|
Haynes Hastelloy® C-22® alloy, all-weld metal, SMAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 24.0 - 427 °C |
7.39 µin/in-°F @Temperature 75.2 - 801 °F |
|
Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 600 °C |
7.39 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl.. |
|||
CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |