Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C @Thickness 6.35 mm |
140 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
PolyOne Geon™ Vinyl Rigid Molding M4825 Polyvinyl Chloride, Rigid (PVC, Rigid) ** NOTE: UL REGULATORY LISTING PENDINGInformation provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C @Thickness 3.18 mm |
140 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ SF M7000 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C @Thickness 3.18 mm |
140 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ SF M7010 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C @Thickness 3.18 mm |
140 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ SF M7020 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C @Thickness 6.40 mm |
140 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Xenoy® 6620 PBT+PC PBT+PC, Unreinforced, impact modified thermoplastic alloy. Outstanding impact at low temperature |