- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 282 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 282 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 4.00 mm |
282 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1200-22 Polycarbonate Resin Description: LUPOY PC 1200-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 4.00 mm |
282 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1300-22 Polycarbonate Resin Description: LUPOY PC 1300-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 4.00 mm |
282 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1301EP22 Polycarbonate Resin Description: LUPOY PC 1301EP-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 4.00 mm |
282 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1301EP-22 Polycarbonate Resin Description: LUPOY PC 1301EP-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 4.00 mm |
282 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1303EP-22 Polycarbonate Resin Description: LUPOY PC 1303EP-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 4.00 mm |
282 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 3010-22 Polycarbonate Resin Description: LUPOY PC 3010-22 resin is designed for injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Character.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 4.00 mm |
282 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1201-22 Polycarbonate Resin Description: LUPOY PC 1201-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 4.00 mm |
282 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1201HP-21 Polycarbonate Resin Description: LUPOY PC 1201HP-21 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 4.00 mm |
282 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1201HP-22 Polycarbonate Resin Description: LUPOY PC 1201HP-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 4.00 mm |
282 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1302HP-21 Polycarbonate Resin Description: LUPOY PC 1302HP-21 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 4.00 mm |
282 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1302HP-22 Polycarbonate Resin Description: LUPOY PC 1302HP-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 6.40 mm |
282 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC LNP* Stat-kon* Lexan_LC1500N compound is a 15% carbon fiber, 6% PTFE reinforced polycarbonate. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 6.40 mm |
282 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Europe-Africa-Middle East) LNP* Stat-kon* Lexan_LCF1506 is a 15% carbon fiber, 6% PTFE reinforced polycarbonate. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C @Thickness 6.40 mm |
282 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Asia Pacific) 15% carbon fiber, 6% PTFE reinforced polycarbonate. |
|||