Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 194 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C @Thickness 6.40 mm	194 °F @Thickness 0.252 in	unannealed; ASTM D648
SABIC Innovative Plastics Cycolac® X11 ABS Automotive: High heat resistance. Excellent flow/impact balance. UL94 HB rated. High gloss.
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C @Thickness 3.20 mm	194 °F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® C2950 PC+ABS Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced flow and impact plus improved heat resistance intended for various applications.
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C @Thickness 3.20 mm	194 °F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® C2950 PC+ABS (Asia Pacific) Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced flow and impact plus improved heat resistance intended for various applications.
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C @Thickness 6.40 mm	194 °F @Thickness 0.252 in	unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® C6200 PC+ABS (Asia Pacific) Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs.
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C @Thickness 6.40 mm	194 °F @Thickness 0.252 in	unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® C6600 PC+ABS Nonbrominated, nonchlorinated FR PC+ABS with balanced flow, impact and hydrolytic stability for a wide variety of applications including business equipment, monitors, enclosures, among others.
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C @Thickness 6.40 mm	194 °F @Thickness 0.252 in	unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® C6600 PC+ABS (Asia Pacific) CYCOLOY C6600 is a FR PC+ABS of nonbrominated, nonchlorinated flame retardant systems with balanced flow, impact and hydrolytic stability for a wide variety of applications including business equipm..
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C @Thickness 6.35 mm	194 °F @Thickness 0.250 in	Annealed; ASTM D648
PolyOne Geon™ HTX M6230 Polyvinyl Chloride Alloy (PVC Alloy) Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C @Thickness 6.40 mm	194 °F @Thickness 0.252 in	unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® C6200 PC+ABS Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs.
Deflection Temperature at 1.8 MPa (264 psi)	90.0 Â°C @Thickness 6.40 mm	194 Â°F @Thickness 0.252 in	ASTM D648
LG Chemical HI121H ABS, High Stiffness Feature: Injection Molding, High StiffnessApplication: Electric & Electronic Products, Miscellaneous GoodsCAS No. 9003-56-9Information provided by LG Chemical
Deflection Temperature at 1.8 MPa (264 psi)	90.0 Â°C @Thickness 6.40 mm	194 Â°F @Thickness 0.252 in	ASTM D648
LG Chemical HI153 ABS, High Flow Feature: Injection Molding, High Flow, Good WeatherabilityApplication: Electric & Electronic Products, Miscellaneous GoodsCAS No. 9003-56-9Information provided by LG Chemical
Deflection Temperature at 1.8 MPa (264 psi)	90.0 Â°C @Thickness 6.40 mm	194 Â°F @Thickness 0.252 in	ASTM D648
LG Chemical HT700 ABS, High Stiffness Feature: Injection Molding, High StiffnessApplication: Electric & Electronic Products, Miscellaneous GoodsCAS No. 9003-56-9Information provided by LG Chemical
Deflection Temperature at 1.8 MPa (264 psi)	90.0 Â°C @Thickness 3.17 mm	194 Â°F @Thickness 0.125 in	Unannealed; ASTM-D648
Ineos ABS LustranÂ® SMA 2171 SMA, Injection Molding Grade LustranÂ® SMA 2171 is a high heat injection molding grade of impact-modified SMA (styrene/maleic anhydride) terpolymer offering an exceptional balance of processability and performance. LustranÂ®..