- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 189 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 189 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® C2950HF PC+ABS Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced impact and heat properties plus improved flow for various applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® C6200 PC+ABS (Asia Pacific) Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C @Thickness 3.18 mm |
189 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| PolyOne Geon™ HTX Ultra LA425 Polyvinyl Chloride Alloy (PVC Alloy) Optimum for Black and Darker Colors below 50L value.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Ductile/Brittle transition as measured by Instrumented Impact is 5 de.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.2 °C @Thickness 3.18 mm |
189 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| PolyOne Geon™ HTX Ultra LA426 Black 2880 Polyvinyl Chloride Alloy (PVC Alloy) Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA426 Black 2880.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® C6200 PC+ABS Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical HF380I ABS, High Flow Feature: Injection Molding, High Flow, Good PaintabilityApplication: Painting Products of Motor Cycle)CAS No. 9003-56-9Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
ASTM D648 |
| LG Chemical HI100 ABS, High Impact Feature: Injection Molding, High ImpactApplication: Helmet, Pipe & Fittings, Miscellaneous Goods)CAS No. 9003-56-9Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
ASTM D648 |
| LG Chemical HI100K ABS, High Impact Feature: Injection Molding, High Impact, Good ProcessingApplication: Miscellaneous Goods)CAS No. 9003-56-9Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical HT700 ABS, High Stiffness Feature: Injection Molding, High StiffnessApplication: Electric & Electronic Products, Miscellaneous GoodsCAS No. 9003-56-9Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 12.7 mm |
189 °F @Thickness 0.500 in |
Unannealed; ASTM-D648 |
| Ineos ABS Lustran® 308 ABS, Medical Grade Lustran® ABS 308 resin is a low gloss, easy-flowing grade of ABS (acrylonitrile butadiene styrene). This injection molding grade offers a good balance of rigidity, impact strength, and abuse resi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl N190A PPE+PS (Asia Pacific) Low heat, flame retardant PPO/HIPS alloy. Internal flammability results only.Not a UL recognised material.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical XG570 MABS, Anti-Scratch, High Impact, High Flow Feature: Injection Molding, Anti-Scratch, High Impact, High FlowApplication: LCD TV Stand Base, Audio/Video HousingCAS No. 9010-94-0Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| LG Chemical XG570 MABS, Anti-Scratch, High Impact, High Flow Feature: Injection Molding, Anti-Scratch, High Impact, High FlowApplication: LCD TV Stand Base, Audio/Video HousingCAS No. 9010-94-0Information provided by LG Chemical |
|||