Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 172 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	77.8 °C @Thickness 3.18 mm	172 °F @Thickness 0.125 in	Compression Molded, Annealed at 60 deg.C; ASTM D648
PolyOne Geon™ Vinyl Rigid Extrusion L4230 Polyvinyl Chloride, Rigid (PVC, Rigid) Extrusion capstock for darker colors. This product is not recommended for horizontal, outdoor applications.Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi)	77.8 °C @Thickness 6.35 mm	172 °F @Thickness 0.250 in	Unannealed; ASTM D648
PolyOne Geon™ HTX M6230 Polyvinyl Chloride Alloy (PVC Alloy) Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi)	77.8 °C @Thickness 3.18 mm	172 °F @Thickness 0.125 in	Annealed; ASTM D648
PolyOne Geon™ Vinyl Dry Blend E7000 Polyvinyl Chloride, Rigid (PVC, Rigid) 60 degree gloss comparisons: Geon E7000 is 47-49;Geon E7456 is 40-49;Geon E7130 is 38-43;Geon E7370 is 26-31Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi)	77.8 °C @Thickness 3.18 mm	172 °F @Thickness 0.125 in	Annealed; ASTM D648
PolyOne Geon™ Vinyl Dry Blend E7001 Polyvinyl Chloride, Rigid (PVC, Rigid) 60 degree gloss comparisons: Geon E7001 is 27-29; Geon E7456 is 40-49; Geon E7130 is 38-43; Geon E7370 is 26-31Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi)	77.8 °C @Thickness 6.35 mm	172 °F @Thickness 0.250 in	Annealed; ASTM D648
PolyOne Geon™ Vinyl Fittings 87322 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi)	78.0 Â°C @Thickness 3.20 mm	172 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics Noryl ENV85 PPE+PS (Asia Pacific) Low heat, flame retardant, extrusion grade PPO/HIPS alloy.Internal flammability results only.Not a UL recognised material.This data was supplied by SABIC-IP for the Asia Pacific region.