| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.573 J/g-°C @Temperature 900 °C |
0.137 BTU/lb-°F @Temperature 1650 °F |
|
| Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.573 J/g-°C @Temperature 900 °C |
0.137 BTU/lb-°F @Temperature 1650 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.573 J/g-°C @Temperature 900 °C |
0.137 BTU/lb-°F @Temperature 1650 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.573 J/g-°C @Temperature 900 °C |
0.137 BTU/lb-°F @Temperature 1650 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.573 J/g-°C @Temperature 900 °C |
0.137 BTU/lb-°F @Temperature 1650 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.573 J/g-°C @Temperature 900 °C |
0.137 BTU/lb-°F @Temperature 1650 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.573 J/g-°C @Temperature 900 °C |
0.137 BTU/lb-°F @Temperature 1650 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.573 J/g-°C @Temperature 900 °C |
0.137 BTU/lb-°F @Temperature 1650 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.573 J/g-°C @Temperature 900 °C |
0.137 BTU/lb-°F @Temperature 1650 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Specific Heat Capacity | 0.575 J/g-°C @Temperature 1000 °C |
0.137 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® B-3® alloy, 20% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Specific Heat Capacity | 0.575 J/g-°C @Temperature 1000 °C |
0.137 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® B-3® alloy, 30% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Specific Heat Capacity | 0.575 J/g-°C @Temperature 1000 °C |
0.137 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® B-3® alloy, 40% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Specific Heat Capacity | 0.574 J/g-°C | 0.137 BTU/lb-°F | |
| Schott N-SSK5 Glass Information Provided by SCHOTT North America, Inc. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.575 J/g-°C @Temperature 1000 °C |
0.137 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes Hastelloy® B-3® alloy, heat treated at 1065°C, rapid quenched The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ea.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, as cast vacuum investment casting Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Specific Heat Capacity | 0.574 J/g-°C @Temperature 700 °C |
0.137 BTU/lb-°F @Temperature 1290 °F |
|
| Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||