Polymer Property : Shear Strength = 80.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	80.0 MPa @Temperature -53.9 °C	11600 psi @Temperature -65.0 °F	Short-Beam, Dry; ASTM D2344
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 120 E-Glass Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Shear Strength	80.0 MPa @Temperature 82.2 °C	11600 psi @Temperature 180 °F	0° Short Beam, Wet
Hexcel® HexPly® 8552 Epoxy Matrix, IM7 Fiber Information provided by HexCel
Shear Strength	80.0 MPa @Temperature 25.0 °C	11600 psi @Temperature 77.0 °F	0° Short Beam, Wet
Hexcel® HexPly® 8552 Epoxy Matrix, SGP196-PW Fiber Information provided by HexCel
Shear Strength	80.0 MPa @Temperature 22.8 °C	11600 psi @Temperature 73.0 °F	ILSS Weft; 10 min @ 250°F
Hexcel® HexPly® EF01 Epoxy Curing System after 1031 2 1000 970 EF01 31% Cure Cycle Information provided by HexCel
Shear Strength	80.0 MPa @Temperature 22.8 °C	11600 psi @Temperature 73.0 °F	ILSS Weft; 15 min @ 250°F
Hexcel® HexPly® EF01 Epoxy Curing System after 1031 2 1000 970 EF01 31% Cure Cycle Information provided by HexCel
Shear Strength	80.0 MPa @Temperature 22.8 °C	11600 psi @Temperature 73.0 °F	ILSS Weft; 30 min @ 250°F
Hexcel® HexPly® EF01 Epoxy Curing System after 1031 2 1000 970 EF01 31% Cure Cycle Information provided by HexCel
Shear Strength	80.0 MPa @Temperature 23.0 °C	11600 psi @Temperature 73.4 °F	0º Interlaminar Shear, 120°C Cure, Conditioning: 23°C; ASTM D2344
Hexcel® HexPly® M47 140°C Curing Epoxy Matrix, Unidirectional Carbon Prepreg M46J Fibre 1947 - 38% resin weight with M46J 52.5% fiber volumeInformation provided by HexCel
Shear Strength	80.0 MPa @Temperature 23.0 °C	11600 psi @Temperature 73.4 °F	0º Interlaminar Shear, Conditioning: 23°C; ASTM D2344
Hexcel® HexPly® M47 140°C Curing Epoxy Matrix, Woven Carbon Prepreg 42% resin weight with C193PW(HTA) - 193 g/m2 plain weave 3K HTA 49% fiber volumeInformation provided by HexCel