Polymer Property : Shear Strength = 2.07 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	2.07 MPa @Temperature 0.000 °C	300 psi @Temperature 32.0 °F	Tensile, Al/Al lap joint; cured 7 days @ 25°C
Abatron AboCast 8110-1/AboCure 8110-3 Flexible Epoxy This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applic..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap
3M Scotch-Weld™ 1838L B/A Two-Part Structural Adhesive Multi-purpose and Rigid bondsInformation provided by 3M
Shear Strength	2.07 MPa @Temperature -53.0 °C	300 psi @Temperature -63.4 °F	Aluminum Overlap
3M Scotch-Weld™ 2214 Non-Metallic Filled Epoxy Adhesive 3M™ Scotch-Weld™ Non-Metallic Filled is a non-metal filled version of Scotch-Weld adhesive 2214 regular. One part 250°F (121°C) curing 100% solids, 3M™ Scotch-Weld™ Epoxy Adhesive 2214 is a pa..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap, Etched Aluminum
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap, Abraded and Solvent Wiped Al
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap, ABS
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap, Etched Aluminum
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap, Abraded and Solvent Wiped Al
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap, ABS
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap, Etched Aluminum
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap, Abraded and Solvent Wiped Al
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap, ABS
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap
3M Scotch-Weld™ DP270 Black Structural Adhesive Rigid potting compound, Non-corrosiveInformation provided by 3M
Shear Strength	2.07 - 2.41 MPa @Temperature 82.0 °C	300 - 350 psi @Temperature 180 °F	Overlap Al/Al (etched); ASTM D1002-72
3M Scotch-Weld™ DP270 Black Structural Adhesive Rigid potting compound, Non-corrosiveInformation provided by 3M
Shear Strength	2.07 MPa @Temperature 82.0 °C	300 psi @Temperature 180 °F	Overlap
3M Scotch-Weld™ DP270 Clear Structural Adhesive Rigid potting compound, Non-corrosiveInformation provided by 3M
Shear Strength	2.07 - 2.41 MPa @Temperature 82.0 °C	300 - 350 psi @Temperature 180 °F	Overlap Al/Al (etched); ASTM D1002-72
3M Scotch-Weld™ DP270 Clear Structural Adhesive Rigid potting compound, Non-corrosiveInformation provided by 3M