Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.680 GPa | 98.6 ksi | 1% Strain Value, From compression molded samples; ASTM D 790 |
NOVA Chemicals Novapol® TR-0535-UI Hexene MDPE Rotational Molding Resin TR-0530-UI complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food. TR-0530-UI is su.. |
|||
Flexural Modulus | 0.680 GPa | 98.6 ksi | 1% Strain Value, From compression molded samples; ASTM D 790 |
NOVA Chemicals Novapol® TR-0535-UIG Hexene MDPE Rotational Molding Resin TR-0530-UIG complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food. TR-0530-UIG is .. |
|||
Flexural Modulus | 0.680 GPa | 98.6 ksi | ISO 178 |
FKuR Kunststoff Bio-Flex® F 2110 Compostable PLA Blend The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta.. |
|||
Flexural Modulus | 0.680 GPa | 98.6 ksi | At 2 mm/min; ISO 178 |
Borealis BorPEX™ ME2592 Medium Density Polyethylene Compound for Crosslinked Pipes (Pex-C (Irradiation)) BorPEXME2592 is a natural, high molecular weight, medium density polyethylene for crosslinkable pipes with excellent flexibility. The compound is especially designed for electron beam irradiation c.. |
|||
Flexural Modulus | 0.680 GPa | 98.6 ksi | ASTM D790 |
Aclo Accucomp Polypropylene CPO402V Automotive Approved Copolymer Extrusion Grade |
|||
Flexural Modulus | 0.680 - 1.60 GPa @Temperature 60.0 - 120 °C |
98.6 - 232 ksi @Temperature 140 - 248 °F |
Average value: 1.13 GPa Grade Count:1 |
Overview of materials for Nylon 6, MoS2 Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, MoS2 Filled". Each property range of values reported is minimum and maximum values of appropria.. |