Flexural Modulus |
9.9133 GPa |
1437.8 ksi |
ASTM D790 |
A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66
Information provided by A. Schulman. |
Flexural Modulus |
9.9133 GPa |
1437.8 ksi |
ASTM D790 |
A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman. |
Flexural Modulus |
9.9133 GPa |
1437.8 ksi |
ASTM D790 |
A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66
Information provided by A. Schulman. |
Flexural Modulus |
9.9133 GPa |
1437.8 ksi |
ASTM D790 |
A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman. |
Flexural Modulus |
9.9133 GPa |
1437.8 ksi |
ASTM D790 |
A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66
Information provided by A. Schulman. |
Flexural Modulus |
9.9133 GPa |
1437.8 ksi |
ASTM D790 |
A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman. |
Flexural Modulus |
9.9133 GPa |
1437.8 ksi |
ASTM D790 |
A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66
Information provided by A. Schulman. |
Flexural Modulus |
9.9133 GPa |
1437.8 ksi |
ASTM D790 |
A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman. |
Flexural Modulus |
9.9133 GPa |
1437.8 ksi |
ASTM D790 |
A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66
Information provided by A. Schulman. |
Flexural Modulus |
9.9133 GPa |
1437.8 ksi |
ASTM D790 |
A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman. |
Flexural Modulus |
9.9133 GPa |
1437.8 ksi |
ASTM D790 |
A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman. |
Flexural Modulus |
9.9133 GPa |
1437.8 ksi |
ASTM D790 |
A. Schulman SCHULAMID® 66 GF33 33% Glass Fiber Reinforced Nylon 66
Information provided by A. Schulman. |