Polymer Property : Rupture Strength = 83.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Rupture Strength	83.0 MPa @Temperature 871 Â°C, Time 3.60e+6 sec	12000 psi @Temperature 1600 Â°F, Time 1000 hour
Haynes 282Â® Nickel Alloy Sheet, Solution Annealed and Age-hardened Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Rupture Strength	83.0 MPa @Temperature 927 Â°C, Time 360000 sec	12000 psi @Temperature 1700 Â°F, Time 100 hour
Haynes 282Â® Nickel Alloy Sheet, Solution Annealed and Age-hardened Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Rupture Strength	83.0 MPa @Temperature 650 Â°C, Time 3.60e+6 sec	12000 psi @Temperature 1200 Â°F, Time 1000 hour	Typical Stress-Rupture
Haynes 75 Nickel Alloy Sheet, Annealed at 1925Â°F (1050Â°C) Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200Â°F (650Â°C). It is principally used in low stress elevated temperature applications requiring reas..
Rupture Strength	83.0 MPa @Temperature 677 °C, Time 3.60e+7 sec	12000 psi @Temperature 1250 °F, Time 10000 hour
ATI Allegheny Ludlum 309 Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo..
Rupture Strength	83.0 MPa @Temperature 677 °C, Time 3.60e+7 sec	12000 psi @Temperature 1250 °F, Time 10000 hour
ATI Allegheny Ludlum 309H Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo..
Rupture Strength	83.0 MPa @Temperature 677 °C, Time 3.60e+7 sec	12000 psi @Temperature 1250 °F, Time 10000 hour
ATI Allegheny Ludlum 309S Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo..
Rupture Strength	83.0 MPa @Temperature 677 °C, Time 3.60e+7 sec	12000 psi @Temperature 1250 °F, Time 10000 hour
ATI Allegheny Ludlum 309Si Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo..
Rupture Strength	83.0 MPa @Temperature 927 °C, Time 360000 sec	12000 psi @Temperature 1700 °F, Time 100 hour
Haynes 282® Nickel Alloy Sheet, Gamma-Prime Strengthened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b..
Rupture Strength	83.0 MPa @Temperature 871 °C, Time 3.60e+6 sec	12000 psi @Temperature 1600 °F, Time 1000 hour
Haynes 282® Nickel Alloy Sheet, Gamma-Prime Strengthened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b..