Polymer Property : Rupture Strength = 79800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Rupture Strength	550 MPa @Temperature 650 Â°C, Time 36000 sec	79800 psi @Temperature 1200 Â°F, Time 10.0 hour	Initial Stress
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750) Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600Â°F (870Â°C). It is widely used as a wrought material for..
Rupture Strength	550 MPa @Temperature 704 Â°C, Time 3.60e+6 sec	79800 psi @Temperature 1300 Â°F, Time 1000 hour
Special Metals UDIMETÂ® alloy R41 Ni-Cr Alloy UDIMETÂ® alloy R41 (UNS N07041) is a precipitation-hardenable nickel-chromium alloy containing significant amounts of cobalt and molybdenum, along with lesser amounts of aluminum and titanium. Al..
Rupture Strength	550 MPa @Temperature 732 °C, Time 720000 sec	79800 psi @Temperature 1350 °F, Time 200 hour
Crucible Compaction Metals P/M Low Carbon Astroloy, Supersolvus P/M Low Carbon Astroloy is often the superalloy of choice when applications require greater ductility along with substantial strength levels. When HIP and heat treatment above the solvus temperatur..