Polymer Property : Rupture Strength = 3630 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Rupture Strength	25.0 MPa @Temperature 800 °C, Time 3.60e+7 sec	3630 psi @Temperature 1470 °F, Time 10000 hour
Outokumpu 153MA™ High Temperature Austenitic Stainless Steel Variant of 1.4301 with increased silicon and nitrogen contents and microalloyed with rare earth metals (REM). This raises the max service temperature in dry air to 1000°C.Applications: Heat and cr..
Rupture Strength	25.0 MPa @Temperature 982 Â°C, Time 3.60e+6 sec	3630 psi @Temperature 1800 Â°F, Time 1000 hour	Plate
Haynes 282Â® Nickel Alloy Sheet, Plate and Bar, Solution Annealed Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Rupture Strength	25.0 MPa @Temperature 870 Â°C, Time 36000 sec	3630 psi @Temperature 1600 Â°F, Time 10.0 hour	Typical Stress-Rupture
Haynes 75 Nickel Alloy Sheet, Annealed at 1925Â°F (1050Â°C) Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200Â°F (650Â°C). It is principally used in low stress elevated temperature applications requiring reas..
Rupture Strength	25.0 MPa @Temperature 982 Â°C, Time 3.60e+6 sec	3630 psi @Temperature 1800 Â°F, Time 1000 hour	Sheet
Special Metals UDIMETÂ® alloy 188 Cobalt-base Alloy UDIMETÂ® alloy 188 (UNS R30188) is a cobalt-base alloy with excellent high-temperature strength and good oxidation resistance to 2000Â°F (1093Â°C). The high chromium level coupled with small ..
Rupture Strength	25.0 MPa @Temperature 900 °C, Time 3.60e+7 sec	3630 psi @Temperature 1650 °F, Time 10000 hour	Stress Rupture
AFE Technologies Cronite 37Ni/18Cr/Nb No. HR32 High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF..
Rupture Strength	25.0 MPa @Temperature 982 °C, Time 3.60e+6 sec	3630 psi @Temperature 1800 °F, Time 1000 hour
Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°..