Polymer Property : Rupture Strength = 250 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Rupture Strength	250 MPa @Temperature 550 °C, Time 3.60e+7 sec	36300 psi @Temperature 1020 °F, Time 10000 hour
Outokumpu 153MA™ High Temperature Austenitic Stainless Steel Variant of 1.4301 with increased silicon and nitrogen contents and microalloyed with rare earth metals (REM). This raises the max service temperature in dry air to 1000°C.Applications: Heat and cr..
Rupture Strength	250 MPa @Temperature 550 °C, Time 3.60e+7 sec	36300 psi @Temperature 1020 °F, Time 10000 hour
Outokumpu 253MA® High Temperature Austenitic Stainless Steel Variant of 1.4828 with increased nitrogen content and has been microalloyed with rare earth metals (REM). The most suitable temperature range is 850-1100°C, because structural changes when used be..
Rupture Strength	250 MPa @Temperature 760 Â°C, Time 3.60e+6 sec	36300 psi @Temperature 1400 Â°F, Time 1000 hour
Special Metals UDIMETÂ® alloy D-979 Fe-Ni Alloy UDIMETÂ® alloy D-979 (UNS N09979) is an iron-nickel alloy designed for turbine disc applications at temperatures up to 1200-1400Â°F (649-760Â°C). Hardened by a complex precipitation of interm..
Rupture Strength	250 MPa @Temperature 500 °C, Time 3.60e+7 sec	36300 psi @Temperature 932 °F, Time 10000 hour
Outokumpu 4948 High Temperature Austenitic Stainless Steel Creep-resistant variant of 1.4301, with a standardized minimum carbon content for service at temperatures of up to 800°C in dry air.Applications: Heat and creep resistance. For use over 550°C for..
Rupture Strength	250 MPa @Temperature 815 °C, Time 338000 sec	36300 psi @Temperature 1500 °F, Time 94.0 hour	forged; 8.4% elong
Special Metals NIMONIC® alloy 91 Ni-Cr-Co Alloy NIMONIC® alloy 91 is a wrought nickel-chromium-cobalt based alloy strengthened by additions of aluminum and titanium.This alloy is a modification of NIMONIC alloy 90, but has an increased chromium ..