Polymer Property : Rupture Strength = 165 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Rupture Strength	165 MPa @Temperature 815 Â°C, Time 36000 sec	23900 psi @Temperature 1500 Â°F, Time 10.0 hour	Initial Stress
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750) Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600Â°F (870Â°C). It is widely used as a wrought material for..
Rupture Strength	165 MPa @Temperature 760 Â°C, Time 3.60e+6 sec	23900 psi @Temperature 1400 Â°F, Time 1000 hour	Sheet
Special Metals UDIMETÂ® alloy 188 Cobalt-base Alloy UDIMETÂ® alloy 188 (UNS R30188) is a cobalt-base alloy with excellent high-temperature strength and good oxidation resistance to 2000Â°F (1093Â°C). The high chromium level coupled with small ..
Rupture Strength	165 MPa @Temperature 760 °C, Time 3.60e+6 sec	23900 psi @Temperature 1400 °F, Time 1000 hour
Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°..