Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Creep Modulus, 1000 hours | 7800 MPa @Strain <=0.500 % |
1.13e+6 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultramid® A3EG10 50% Glass Filled PA66 (Conditioned) Description: 50% glass-fiber reinforced injection-molding grade for technical articles of very high stiffness as well as for electric insulating parts.Information provided by BASF |
|||
Tensile Creep Modulus, 1000 hours | 7800 MPa @Strain <=0.500 % |
1.13e+6 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultramid® A3WG10 BK 00564 50% Glass Filled PA66 (Conditioned) Description: 50% glass-fiber reinforced injection-molding grade with high heat aging resistance for technical articles of very high stiffness.Information provided by BASF |