Polymer Property : Tensile Strength, Ultimate = 995 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	995 MPa	144000 psi
Haynes 214Â® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	995 MPa	144000 psi
Haynes 230Â® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Ultimate	995 MPa @Temperature 650 Â°C	144000 psi @Temperature 1200 Â°F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370Â°C (700Â°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	995 MPa	144000 psi
Haynes 25 alloy, room temperature after 0% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..