Polymer Property : Tensile Strength, Ultimate = 975 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	975 MPa	141000 psi
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175Â°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Ultimate	975 MPa	141000 psi
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175Â°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Ultimate	975 MPa	141000 psi
Haynes 214Â® alloy sheet Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	975 MPa	141000 psi
Haynes 625 alloy, 40% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Ultimate	975 MPa	141000 psi
Haynes 625 alloy, 50% cold reduction, 1010Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Ultimate	975 MPa	141000 psi
Haynes 625 alloy, 50% cold reduction, 1065Â°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..