Polymer Property : Tensile Strength, Ultimate = 900 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	900 - 1100 MPa	131000 - 160000 psi	After Post Sintering Heat Treatment
MarkeTech 90-7-3 Tungsten Alloy, AMS-T-21014 Class 1 Used to fabricate parts to near net size and several processes to produce high quality tungsten based materials.Tungsten heavy alloys have very high melting point and have a density twice that of st..
Tensile Strength, Ultimate	900 - 1000 MPa	131000 - 145000 psi	Sintered Only
MarkeTech 91-6-3 Tungsten Alloy, AMS-T-21014 Class 1 Used to fabricate parts to near net size and several processes to produce high quality tungsten based materials.Tungsten heavy alloys have very high melting point and have a density twice that of st..
Tensile Strength, Ultimate	900 - 1100 MPa	131000 - 160000 psi	Sintered Only
MarkeTech 92-5-3 Tungsten Alloy, AMS-T-21014 Class 2 Used to fabricate parts to near net size and several processes to produce high quality tungsten based materials.Tungsten heavy alloys have very high melting point and have a density twice that of st..
Tensile Strength, Ultimate	900 - 1100 MPa	131000 - 160000 psi	Sintered Only
MarkeTech 93-4-3 Tungsten Alloy, AMS-T-21014 Class 2 Used to fabricate parts to near net size and several processes to produce high quality tungsten based materials.Tungsten heavy alloys have very high melting point and have a density twice that of st..
Tensile Strength, Ultimate	900 MPa @Temperature 760 Â°C	131000 psi @Temperature 1400 Â°F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121Â°C, air cooled, aged 16 hours at 899Â°C Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Tensile Strength, Ultimate	900 MPa	131000 psi
Haynes 25 alloy, room temperature sheet after 2500 hours of 650Â°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	>= 900 MPa	>= 131000 psi
TIMET TIMETAL® 367 (Ti-6Al-7Nb) Titanium Alloy Medium-Strength Surgical Implant AlloyFeatures: TIMETAL 367 is a dedicated, medium strength, titanium alloy for surgical implants. The alloy was developed specifically for the manufacture of femora..
Tensile Strength, Ultimate	900 MPa	131000 psi	As-HIP
Crucible Compaction Metals P/M 625M Corrosion Resistant Alloy P/M 625M (chemically, UNS N07626) is produced by the state-of-the-art Crucible P/M process: inert gas atomization, coupled with consolidation by hot isostatic pressing (HIP) and/or extrusion. The a..
Tensile Strength, Ultimate	900 MPa	131000 psi
Ametek 17-4 P/M Process, Sintered at 2300°F (1260°C) Composition reported is typical of 17-4 precipitation hardening stainless. This alloy is widely used because of its high strength, high hardness, excellent corrosion resistance, and easy heat treat..
Tensile Strength, Ultimate	900 - 1100 MPa	131000 - 160000 psi	Rm
Assab Steels 705M Machinery Steel ASSAB 705M is an alloyed machinery steel with good hardenability also in heavier sizes. As standard ASSAB 705M is supplied tough hardened with no further heat treatment required. It can be oil harde..
Tensile Strength, Ultimate	900 MPa	131000 psi
ATI Allegheny Ludlum AL 15-7 High Strength Stainless Steel, UNS S15700 Property data below is typical of annealed samples. Available in sheet and strip. For use in high-strength springs, bellows, and aerospace applications.Information provided by Allegheny Ludlum
Tensile Strength, Ultimate	900 MPa	131000 psi
ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 10% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co..
Tensile Strength, Ultimate	900 MPa	131000 psi
Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..