Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 795 MPa @Temperature 650 °C |
115000 psi @Temperature 1200 °F |
|
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Ultimate | 795 MPa | 115000 psi | |
Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Ultimate | 795 MPa | 115000 psi | |
Haynes 556® alloy, 0% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Ultimate | 795 MPa @Temperature 205 °C |
115000 psi @Temperature 401 °F |
|
Haynes Hastelloy® B-3® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Tensile Strength, Ultimate | 795 MPa | 115000 psi | |
ATI Allegheny Ludlum AL 219 High Strength Specialty Steel Alloy (Alloy 21-6-9), UNS S21904 Property data below is typical of annealed samples. Available in sheet, strip and plate. Intended for high-strength non-magnetic applications and aircraft parts such as hydraulic tubing.Informatio.. |