Polymer Property : Tensile Strength, Ultimate = 330 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	330 MPa @Temperature 500 °C	47900 psi @Temperature 932 °F	EN min.; EN 10002-5
Outokumpu 4878 High Temperature Austenitic Stainless Steel Heat-resistant variant of 1.4541, with a slightly higher max carbon content. Recommended max service temperature for this steel in dry air is 800°C. Applications: Heat and creep resistance. For ..
Tensile Strength, Ultimate	330 MPa @Temperature 870 Â°C	47900 psi @Temperature 1600 Â°F
Haynes HastelloyÂ® W alloy as a weld filler, base metal Alloy 625/ Alloy 718 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica..
Tensile Strength, Ultimate	330 MPa @Temperature 870 Â°C	47900 psi @Temperature 1600 Â°F
Haynes 556Â® alloy, cold rolled, solution annealed sheet, 0.8-2.8 mm thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	330 - 400 MPa	47900 - 58000 psi
SSAB Tunnplat DocolÂ® 220 YP High-strength Steel High-strength SteelComments: Docol YP - Cold Rolled Steel - HSLA. Property values are for cold-rolled steel; thicknesses 0.5 - 3.00 mm. Iron content is approximate - exact composition is not report..
Tensile Strength, Ultimate	>= 330 MPa	>= 47900 psi
AK Steel Cold Rolled Carbon Steel, Dent Resistant (DR 210), SAE J2340 Type 210 A Information provided by AK Steel
Tensile Strength, Ultimate	330 MPa	47900 psi
AK Steel Hot Rolled Carbon Steel, Drawing Steel (DS Type B), Standard Grade DS is made by adding aluminum to the molten steel and may be used in drawing applications.Information provided by AK Steel
Tensile Strength, Ultimate	330 MPa	47900 psi
AK Steel Hot Rolled Carbon Steel, Drawing Steel with Boron (DS Type B), Standard Grade DS is made by adding aluminum and boron to the molten steel and may be used in severe drawing applications.Information provided by AK Steel
Tensile Strength, Ultimate	>= 330 MPa	>= 47900 psi
AK Steel Type 1 & 2, Grade 33 Cold Rolled Carbon Steel, Structural Steel (SS) Information provided by AK Steel
Tensile Strength, Ultimate	>= 330 MPa	>= 47900 psi
Aleris Alustar Aluminum Alloy, O/H111 At least 20% stronger than AA 5083 before and after welding. Bendability and weldability similar to AA 5083. High corrosion resistance. Provides options for ship design and building.Composition d..