Polymer Property : Tensile Strength, Ultimate = 3150 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	21.7 MPa	3150 psi	ASTM D638-95
Multibase Multi-Pro® 3216 CUW BLK Polypropylene Multi-Pro 3216 CUW BLK is well suited for resin furniture requiring high impact strength and stiffness at moderate cost.Data provided by Multibase.
Tensile Strength, Ultimate	21.7 MPa	3150 psi	ASTM D412-80
DuPont Performance Polymers Hypalon® 4085 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound Carbon black compound with 100 parts Hypalon; 27.8 parts sublimed litharge dispersion; 55 parts carbon black; 55 parts aromatic process oil; 0.5 parts MTBS; and 2 parts Tetrone® A rubber accelerato..
Tensile Strength, Ultimate	21.7 MPa	3150 psi
Colorite Polymers Self Frosting™ 9511SF Vinyl Compound Description: Colorite has developed a family of vinyl compounds to satisfy the needs of those who need a smooth, low gloss, low friction surface for the products that they produce. Historically, thi..
Tensile Strength, Ultimate	21.7 MPa	3150 psi	ASTM D638
Colorite Polymers 9273E General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r..
Tensile Strength, Ultimate	21.7 MPa	3150 psi
Colorite Polymers 9511 Clear Extrusion Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for the extrusion of various components for the production of devices. The vinyl components used in pre..
Tensile Strength, Ultimate	21.7 MPa	3150 psi
Colorite Polymers 9512 Clear Injection Molding Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for injection molding of various components such as drip chambers, connectors, valves, etc. The vinyl c..
Tensile Strength, Ultimate	21.7 MPa	3150 psi	ASTM D412
DuPont Performance Polymers Kalrez® 3018 FFKM Perfluoroelastomer (discontinued **) A carbon black-filled compound that is similar to Compound 1050LF, except for higher hardness/modulus. Best hot water/steam resistance. Generally used in oil fields and process industry application..