Polymer Property : Tensile Strength, Ultimate = 181000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1150 - 1250 MPa	167000 - 181000 psi	Swaged after Sintering
MarkeTech 91-6-3 Tungsten Alloy, AMS-T-21014 Class 1 Used to fabricate parts to near net size and several processes to produce high quality tungsten based materials.Tungsten heavy alloys have very high melting point and have a density twice that of st..
Tensile Strength, Ultimate	1150 - 1250 MPa	167000 - 181000 psi	Swaged after Sintering
MarkeTech 92-5-3 Tungsten Alloy, AMS-T-21014 Class 2 Used to fabricate parts to near net size and several processes to produce high quality tungsten based materials.Tungsten heavy alloys have very high melting point and have a density twice that of st..
Tensile Strength, Ultimate	1150 - 1250 MPa	167000 - 181000 psi	ASwaged after Sintering
MarkeTech 93-4-3 Tungsten Alloy, AMS-T-21014 Class 2 Used to fabricate parts to near net size and several processes to produce high quality tungsten based materials.Tungsten heavy alloys have very high melting point and have a density twice that of st..
Tensile Strength, Ultimate	1030 - 1250 MPa	149000 - 181000 psi
Materion Beryllium Copper Alloy 165 Forgings & Extrusions; AT (TF00) Temper (UNS C17000) Treatment required for max strength: 3 hrs @ 330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In..
Tensile Strength, Ultimate	1140 - 1250 MPa	165000 - 181000 psi	Solution Annealed & Aged
Materion Beryllium Copper Alloy 245C Castings (UNS C82600) Pouring Temperature: 970-1065Â°CHeat treatment required for max strength (Annealing): 760-790Â°C/water quenchHeat treatment required for max strength (Hardening): 760-790Â°C/water quenchTabula..
Tensile Strength, Ultimate	1140 - 1250 MPa	165000 - 181000 psi	Solution Annealed & Aged
Materion Beryllium Copper Alloy 245CT Castings (UNS C82600) Pouring Temperature: 970-1065Â°CHeat treatment required for max strength (Annealing): 760-790Â°C/water quenchHeat treatment required for max strength (Hardening): 760-790Â°C/water quenchTabula..