Polymer Property : Tensile Strength, Ultimate = 16.2 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	16.2 MPa	2350 psi
Sylvin Technologies 8600-75 Clear PVC Extrusion Compound Information provided by Sylvin Technologies Inc.
Tensile Strength, Ultimate	16.2 MPa	2350 psi
Sylvin Technologies 8950-85 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc.
Tensile Strength, Ultimate	16.2 MPa	2350 psi
Sylvin Technologies 9600-75 Clear PVC Molding Compound Information provided by Sylvin Technologies Inc.
Tensile Strength, Ultimate	16.2 MPa	2350 psi
Sylvin Technologies 9950-85 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc.
Tensile Strength, Ultimate	16.2 MPa	2350 psi	Die C (35 min / 145°C); ASTM D412
Dow SE BR-1220M Stereospecific high cis-1,4 Polybutadiene (BR) SE BR-1220M is manufactured by a solution process using cobalt catalyst which produces polymers with a very light color and low ash content. A non-staining stabilizer is added during the production..
Tensile Strength, Ultimate	16.2 MPa	2350 psi	ASTM D638
Colorite Polymers 8033 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r..
Tensile Strength, Ultimate	16.2 MPa	2350 psi	ASTM D638
Colorite Polymers 8033SF General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r..
Tensile Strength, Ultimate	16.2 MPa	2350 psi	Cured 7 min at 177°C and Post Cured 2 hr at 232°C
DuPont Performance Polymers VTR 8505 Peroxide Cured Fluoroelastomer (FKM) Formulation (discontinued **) FormulationViton® 8505