Polymer Property : Tensile Strength, Ultimate = 158000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1090 MPa	158000 psi
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065Â°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Ultimate	1090 MPa	158000 psi
Haynes 214Â® alloy, 50% cold reduction, 980Â°C (1800Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	1090 MPa	158000 psi
Haynes 214Â® alloy, sheet, 100 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	1090 MPa	158000 psi	Typical
TIMET 6-6-2 Titanium Alloy (Ti-6Al-6V-2Sn), Annealed Features: TIMETAL 6-6-2 offers improved strength properties and greater depth hardenability compared with TIMETAL 6-4.Data provided by TIMET.