Polymer Property : Tensile Strength, Ultimate = 148700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1025 MPa	148700 psi
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065Â°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Ultimate	1025 MPa	148700 psi
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120Â°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Ultimate	1025 MPa @Temperature 540 Â°C	148700 psi @Temperature 1000 Â°F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595Â°C (1100Â°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	1025 MPa @Thickness 4.762 mm	148700 psi @Thickness 0.1875 in	Typical for Plate, 1/4-Hard, Transverse
AK Steel NITRONIC® 30 Austenitic Stainless Steel AK Steel NITRONIC 30 Stainless Steel offers significantly higher strength than Type 304 and potential for applications requiring good resistance to aqueous and atmospheric corrosion resistance combi..