Polymer Property : Tensile Strength, Ultimate = 1420 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1420 MPa	206000 psi
Haynes HastelloyÂ® C-22Â® alloy, 40% cold worked sheet, aged 100 hours at 500Â°C HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Ultimate	1420 MPa	206000 psi
Haynes HastelloyÂ® C-22Â® alloy, 50% cold worked sheet HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Ultimate	1420 MPa	206000 psi	45 HRC, Round bar 1" diameter, Hardened in oil from 1880°F and tempered twice
EDRO #8 Premium 420 Stainless Mold Steel EDRO #8™ is a chromium-alloyed stainless tool steel with the following properties: excellent corrosion resistance, superior polishability, good wear resistance, good machinability, and stability in..
Tensile Strength, Ultimate	1420 MPa	206000 psi	hardened to 45 HRC
Bohler-Uddeholm ORVAR® 2M / AISI H13 Hot Work Tool Steel Orvar 2 Microdized is a chromium-molybdenum-vanadium alloyed steelORVAR® 2M / AISI H13 is a conventionally produced hot work tool steel with overall good ductility, toughness, wear resistance, hard..
Tensile Strength, Ultimate	1420 MPa	206000 psi	hardness of 45 HRC
Bohler-Uddeholm UDDEHOLM ORVAR® SUPERIOR (Premium AISI H13) Hot Work Tool Steel Chromium-molybdenum-vanadium alloyed steelA premium Cr-Mo-V-alloyed hot work die steel with good resistance to thermal fatigue. The steel is produced by a special melting and refining technique in o..
Tensile Strength, Ultimate	1420 MPa	206000 psi	hardness of 45 HRC
Bohler-Uddeholm UDDEHOLM ORVAR® SUPREME (Premium AISI H13) Hot Work Tool Steel Chromium-molybdenum-vanadium alloyed steelA premium Cr-Mo-V-alloyed hot work die steel with good resistance to thermal fatigue. The steel is produced by a special melting and refining technique in o..
Tensile Strength, Ultimate	1420 MPa	206000 psi	hardened to 45 HRC
Bohler-Uddeholm UDDEHOLM STAVAX® ESR Modified 420 Premium grade stainless tool steelStavax® ESR is characterized by: Good corrosion resistance Good polishability Good wear resistance Good machinability Good stability in hardeningApplications: Udd..
Tensile Strength, Ultimate	1420 MPa	206000 psi	R<sub>m</sub>. 45 HRC.
Assab Steels 8407 2M Hot Work Steel ASSAB 8407 is a chromium-molybdenum-vanadium-alloyed steel which is characterized by: Good resistance to abrasion at both low and high temperatures. High level of toughness and ductility Uniform ..
Tensile Strength, Ultimate	1420 MPa	206000 psi	R<sub>m</sub>. 45 HRC.
Assab Steels 8407 SUPREME Hot Work Steel 8407 SUPREME is characterized by:High level of resistance to thermal shock and thermal fatigueGood high temperature strengthExcellent toughness and ductility in all directionsGood machinability and ..