Polymer Property : Tensile Strength, Ultimate = 1005 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	1005 MPa	145800 psi
Haynes 188 alloy, plate at RT after 0 hours at 870Â°C (1600Â°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Ultimate	1005 MPa	145800 psi
Haynes 188 alloy, plate at RT after 16000 hours at 870Â°C (1600Â°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Ultimate	1005 MPa	145800 psi
Haynes 214Â® alloy, 10% cold reduction, 925Â°C for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	1005 MPa	145800 psi
Haynes 214Â® alloy, 20% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	1005 MPa	145800 psi
Haynes 230Â® alloy, 40% cold reduction, 1066Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Ultimate	1005 MPa	145800 psi
Haynes 25 alloy, cold rolled and 1205Â°C (2200Â°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	1005 MPa	145800 psi
Haynes 625 alloy, plate after 4000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..