Polymer Property : Fatigue Strength = 414 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Fatigue Strength	414 MPa @# of Cycles 1.00e+6	60000 psi @# of Cycles 1.00e+6	R = -1, 105 ksi YS
Materion ToughMetÂ® T3 AT110 (OD≥4") ToughMetÂ® is Brush Wellman's solution for severe service material problems. By applying their EquaCastÂ® process, tailored alloying additions and spinodal hardening technology, they have e..
Fatigue Strength	414 MPa @# of Cycles 1.00e+6	60000 psi @# of Cycles 1.00e+6	R = -1, 105 ksi YS
Materion ToughMetÂ® T3 AT120 (OD≥4") ToughMetÂ® is Brush Wellman's solution for severe service material problems. By applying their EquaCastÂ® process, tailored alloying additions and spinodal hardening technology, they have e..
Fatigue Strength	414 MPa @# of Cycles 1.00e+6	60000 psi @# of Cycles 1.00e+6	R = -1, 105 ksi YS
Materion ToughMetÂ® T3 AT120 (OD ToughMetÂ® is Brush Wellman's solution for severe service material problems. By applying their EquaCastÂ® process, tailored alloying additions and spinodal hardening technology, they have e..
Fatigue Strength	414 MPa @# of Cycles 1.00e+6	60000 psi @# of Cycles 1.00e+6	R = -1, 105 ksi YS
Materion ToughMetÂ® T3 AT90 (OD≥4") ToughMetÂ® is Brush Wellman's solution for severe service material problems. By applying their EquaCastÂ® process, tailored alloying additions and spinodal hardening technology, they have e..
Fatigue Strength	414 MPa @# of Cycles 1.00e+6	60000 psi @# of Cycles 1.00e+6	R = -1, 105 ksi YS
Materion ToughMet® T3 AT110 (OD ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have engin..
Fatigue Strength	414 MPa @# of Cycles 1.00e+6	60000 psi @# of Cycles 1.00e+6	R = -1, 105 ksi YS
Materion ToughMet® T3 AT90 (OD ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have engin..