Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 480 MPa @Thickness 101.6 - 127 mm |
69600 psi @Thickness 4.000 - 5.00 in |
Typical Strength |
Constellium Alumold® 350 Aluminum Alumold-350® has been specifically developed to achieve the best combination of strength at low and high temperatures, together with a good shape stability and machinability. Alumold-350® is parti.. |
|||
Tensile Strength | 480 MPa @Thickness 450 - 700 mm |
69600 psi @Thickness 17.7 - 27.6 in |
long-transverse direction |
Constellium Alumold® 500 Forged Aluminum Forged thick blocks in Alumold® 500 have been developed to provide high and consistent strength across the thickness, good dimensional stability and excellent machinability, in order to respond to .. |
|||
Tensile Strength | 480 MPa @Thickness 450 - 700 mm |
69600 psi @Thickness 17.7 - 27.6 in |
Temper T652 |
Constellium Certal® SPC Forged Aluminum Certal® SPC forged has been optimized to provide excellent machinability, good shape stability and high strength properties throughout the plate thickness. Uniform strength is an important property.. |
|||
Tensile Strength | >= 480 MPa @Thickness 120 - 140 mm |
>= 69600 psi @Thickness 4.72 - 5.51 in |
|
Constellium Fortal® Aluminum Alloy Fortal® plates are optimized to provide high mechanical strength, combined with good shape stability and excellent machinability. Typical applications include sheet forming tools, base plates for m.. |
|||
Tensile Strength | >= 480 MPa @Thickness 160 - 180 mm |
>= 69600 psi @Thickness 6.30 - 7.09 in |
|
Constellium Fortal® Aluminum Alloy Fortal® plates are optimized to provide high mechanical strength, combined with good shape stability and excellent machinability. Typical applications include sheet forming tools, base plates for m.. |