Polymer Property : Tensile Strength = 59500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	>= 410 MPa @Thickness 450 - 700 mm	>= 59500 psi @Thickness 17.7 - 27.6 in	long-transverse direction
Constellium Alumold® 500 Forged Aluminum Forged thick blocks in Alumold® 500 have been developed to provide high and consistent strength across the thickness, good dimensional stability and excellent machinability, in order to respond to ..
Tensile Strength	>= 410 MPa @Thickness 450 - 700 mm	>= 59500 psi @Thickness 17.7 - 27.6 in	Temper T652
Constellium Certal® SPC Forged Aluminum Certal® SPC forged has been optimized to provide excellent machinability, good shape stability and high strength properties throughout the plate thickness. Uniform strength is an important property..
Tensile Strength	410 MPa @Thickness 15.0 - 35.0 mm	59500 psi @Thickness 0.591 - 1.38 in	Typical Strength
Constellium Unidal® High-Strength Rolled Precision Aluminum Plate, Milled Both Sides Unidal® precision plates offers a combination of dimensional stability and high mechanical strength. The very low internal stress reduces the risk of deformation during machining, thereby reducing ..
Tensile Strength	410 MPa @Thickness 60.0 - 80.0 mm	59500 psi @Thickness 2.36 - 3.15 in	Typical Strength
Constellium Unidal® High-Strength Rolled Precision Aluminum Plate, Milled Both Sides Unidal® precision plates offers a combination of dimensional stability and high mechanical strength. The very low internal stress reduces the risk of deformation during machining, thereby reducing ..
Tensile Strength	>= 410 MPa @Thickness 5.90 - 15.0 mm	>= 59500 psi @Thickness 0.232 - 0.591 in	Temper T651
Constellium Unidal® High-Strength Rolled Precision Aluminum Plate, Milled Both Sides Unidal® precision plates offers a combination of dimensional stability and high mechanical strength. The very low internal stress reduces the risk of deformation during machining, thereby reducing ..