Polymer Property : Modulus of Rupture = 0.200 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Modulus of Rupture 0.00138 - 0.00276 GPa

@Treatment Temp. 816 °C,
Time 18000 sec
0.200 - 0.400 ksi

@Treatment Temp. 1500 °F,
Time 5.00 hour
ASTM C133
Thermal Ceramics Kaocast 3000 Dense Castable
Kaocast is an alumina-silica refractory castable capable of withstanding up to 3000°F (1649°C). It possesses excellent volume stability. Many furnace operators select Kaocast for all purpose servi..
Modulus of Rupture 0.00138 - 0.00345 GPa

@Treatment Temp. 816 °C,
Time 18000 sec
0.200 - 0.500 ksi

@Treatment Temp. 1500 °F,
Time 5.00 hour
ASTM C133
Thermal Ceramics Kaocrete 28-LI Dense Castable
Kaocrete 28-LI is a general-purpose, low iron monolithic which contains an intermediate-purity calcium aluminate cement that can be cast or gunned into place. Designed for applications up to 2800°F..
Modulus of Rupture 0.00138 - 0.00414 GPa
0.200 - 0.600 ksi
Dried 18-24 hours at 220°F; ASTM C133
Thermal Ceramics Kaocrete B Dense Castable
Kaocrete B is a more plastic material than most refractory castables. It is an excellent plastering material, preferred for patching linings and baffles. Recommended only for relatively thin section..
Modulus of Rupture 0.00138 - 0.00276 GPa

@Treatment Temp. 1200 °C,
Time 18000 sec
0.200 - 0.400 ksi

@Treatment Temp. 2200 °F,
Time 5.00 hour
ASTM C133
Thermal Ceramics Kaocrete B Dense Castable
Kaocrete B is a more plastic material than most refractory castables. It is an excellent plastering material, preferred for patching linings and baffles. Recommended only for relatively thin section..
Modulus of Rupture 0.00138 GPa
0.200 ksi
dried
Thermal Ceramics Kaofil HT Pumpable
Kaofil Pumpables are a mixture of Kaowool ceramic fibers and fillers dispersed in a high-temperature binder. This mix produces a stable high-temperature insulation which can be placed by forced pump..
Modulus of Rupture 0.00138 GPa
0.200 ksi
dried
Thermal Ceramics Kaofil XTP Pumpable
Kaofil Pumpables are a mixture of Kaowool ceramic fibers and fillers dispersed in a high-temperature binder. This mix produces a stable high-temperature insulation which can be placed by forced pump..
Modulus of Rupture 0.00138 - 0.00276 GPa

@Treatment Temp. 816 °C,
Time 18000 sec
0.200 - 0.400 ksi

@Treatment Temp. 1500 °F,
Time 5.00 hour
ASTM C133
Thermal Ceramics Kaogun 26 Dense Gunning Castables
Kaogun 26 is a general purpose 2600°F (1427°C) gunning castable designed for minimal rebound. It is excellent for use in hot and cold gunning repair. It can also be troweled or plastered for repai..
Modulus of Rupture 0.00138 - 0.00241 GPa

@Treatment Temp. 1200 °C,
Time 18000 sec
0.200 - 0.350 ksi

@Treatment Temp. 2200 °F,
Time 5.00 hour
ASTM C133
Thermal Ceramics Kaolite 2200-HS Gunning Insulation Castables
Kaolite 2200-HS Gun is a high-strength, lightweight castable designed for easy gunite placement (very low rebound). Kaolite 2200-HS Gun has excellent volume stability up to 2200°F (1204°C) and goo..
Modulus of Rupture 0.00138 - 0.00207 GPa

@Treatment Temp. 1200 °C,
Time 18000 sec
0.200 - 0.300 ksi

@Treatment Temp. 2200 °F,
Time 5.00 hour
ASTM C133
Thermal Ceramics Kaolite 2200-HS Insulation Castables
Kaolite 2200-HS is a medium weight, high strength castable that resists thermal shock, and has excellent volume stability.Features:Light weight and low thermal conductivity reduce both the quantity ..
Modulus of Rupture 0.00138 - 0.00241 GPa

@Treatment Temp. 816 °C,
Time 18000 sec
0.200 - 0.350 ksi

@Treatment Temp. 1500 °F,
Time 5.00 hour
ASTM C133
Thermal Ceramics Kaolite 2800 High Temperature Insulating Castables
Kaolite 2800 is a general-purpose insulating castable for use at temperatures up to 2800°F (1538°C). It may be cast, gunited, or troweled in place. It contains a high-purity, calcium-aluminate cem..
Modulus of Rupture 0.00138 - 0.00172 GPa
0.200 - 0.250 ksi
Thermal Ceramics Kaowool PM Low Temperature Board
Kaowool PM is manufactured to close tolerances with an excellent surface finish. Kaowool PM has a good thermal conductivity and can easily be die-cut.Features: Excellent thermal conductivity Capabil..
Modulus of Rupture 0.00138 - 0.00172 GPa
0.200 - 0.250 ksi
Thermal Ceramics Superwool 607 PM Board
Superwool 607 PM boards are processed from a slurry consisting of Superwool bulk and organic binders. This board product is noted for its excellent surface finish, thickness uniformity and high insu..
Modulus of Rupture 0.00138 GPa
0.200 ksi
Thermal Ceramics TC-26 High Temperature Insulating Firebrick
The bond developed is a ceramic bond that is formed by high temperature firing. This produces bricks that are very stable and strong at temperatures higher than 2600°F (1427°C). Features:High temp..
Modulus of Rupture 0.00138 GPa
0.200 ksi
Parallel to Thickness
Zircar Ceramics AL-25/1700 Alumina Insulation
AL-25/1700 is a rigid medium duty grade of alumina fiber board. Not as strong as SALI but capable of delivering years of service.Information provided by Zircar Ceramics.
Modulus of Rupture 0.00138 GPa
0.200 ksi
Green (typ.)
Unifrax Fiberfrax® Duraboard® LD Ceramic Fiber Board
Fiberfrax® Duraboard® products are a family of rigid, high-temperature ceramic fiber boards manufactured in a wet forming process using Fiberfrax alumina-silica fibers and binders. All Duraboard ..
Modulus of Rupture 0.00138 - 0.00207 GPa
0.200 - 0.300 ksi
Dried 18-24 hours at 220°F; ASTM C133
Thermal Ceramics Kaolite 2500-LI Insulation Castables
Kaolite 2500-LI is a high-strength lightweight castable that contains an intermediate-purity calcium-aluminate cement. Total iron oxide contents of 0.9% enables use where hydrogen or reducing atmosp..
Modulus of Rupture 0.00138 - 0.00207 GPa

@Treatment Temp. 1370 °C,
Time 18000 sec
0.200 - 0.300 ksi

@Treatment Temp. 2500 °F,
Time 5.00 hour
ASTM C133
Thermal Ceramics Kaolite 2500-LI Insulation Castables
Kaolite 2500-LI is a high-strength lightweight castable that contains an intermediate-purity calcium-aluminate cement. Total iron oxide contents of 0.9% enables use where hydrogen or reducing atmosp..
Modulus of Rupture 0.00138 - 0.00207 GPa

@Treatment Temp. 816 °C,
Time 18000 sec
0.200 - 0.300 ksi

@Treatment Temp. 1500 °F,
Time 5.00 hour
ASTM C133
Thermal Ceramics Kaolite 3000 High Temperature Insulating Castables
Kaolite 3000 is a lightweight 60% alumina insulating castable for use up to 3000°F (1649°C) that is specifically designed for gunning or casting. This mix utilizes a high-purity calcium-aluminate ..