Polymer Property : Tensile Strength, Ultimate = 81900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	565 MPa @Thickness 12.7 mm, Temperature 871 Â°C	81900 psi @Thickness 0.500 in, Temperature 1600 Â°F	As Welded, Solution Annealed, and Aged; Weld/Weld Fracture
Haynes 282Â® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Tensile Strength, Ultimate	565 MPa @Diameter 12.7 mm, Temperature 450 Â°C	81900 psi @Diameter 0.500 in, Temperature 842 Â°F
Haynes HastelloyÂ® C-2000Â® Nickel Alloy Shielded Metal Arc Welded (SMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Ultimate	565 MPa @Thickness 50.8 - 152 mm	81900 psi @Thickness 2.00 - 6.00 in	at center (L/T direction)
Alcoa QC-10® Aluminum Mold Alloy Specifically designed for high production injection and blow mold applications, QC-10 offers outstanding strength, stability, and durability. Its improved alloy composition provides outstanding, 1"-..
Tensile Strength, Ultimate	565 MPa @Thickness 12.7 mm, Temperature 538 °C	81900 psi @Thickness 0.500 in, Temperature 1000 °F
Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..